CONSTRUCTION
Style 2007 packing is an interlock braid, utilizing Teadit's EG2 PTFE/graphite yarn and a high temperature brek-in lubricant. EG2 yarn is formed from expanded PTFE in which fine particles of pure graphite have been encapsulated. The resulting packing combines the chemical resistance of PTFE with the heat dissipation characteristics of graphite, thus allowing much higher shaft speeds than conventional PTFE packings.
APPLICATION/SERVICE
Style 2007 is chemically inert over themore
CONSTRUCTION
Style 2007 packing is an interlock braid, utilizing Teadit's EG2 PTFE/graphite yarn and a high temperature brek-in lubricant. EG2 yarn is formed from expanded PTFE in which fine particles of pure graphite have been encapsulated. The resulting packing combines the chemical resistance of PTFE with the heat dissipation characteristics of graphite, thus allowing much higher shaft speeds than conventional PTFE packings.
APPLICATION/SERVICE
Style 2007 is chemically inert over the entire 0-14 pH range with these exceptions: molten alkali metals, flourides, aleum, fuming nitric acid, aqua regia, and other strong oxidizing agents. This style is an excellent general service and corrosive service packing. It is commonly used in pumps, valves, rotating and reciprocating shafts, mixers and agitators, and is especially designed for services involving surface speeds and temperatures higher than those that can be handled by pure PTFE packing.
SERVICE LIMITS
Temperature limits
Minimum: -328°F (-200°C)
Maximum: 540°F (280°C)
Pressure limits:
Rotating: 500 psi (35 bar)
Reciprocating: 1450 psi (100 bar)
Static: 2900 psi (200 bar)
Shaft Speed: 4900 fpm (25 m/s)
pH: 0-14